Inconel 600 Forging

Short Description:

Specifications of Inconel 600 Forging: Grade 600,601,625,690 etc. Specifications ASTM B564, AMS 5665 International Specifications BS 3072-3076 (NA14) DIN 17742, DIN 17750, DIN 17754 WERKSTOFF Nr 2.4816 TÜV 305 AFNOR-NC 15 Fe Other Type Of 600 Forged: Inconel 600 Equivalent For Forgings: STANDARD WERKSTOFF NR. UNS JIS GOST EN OR 600 2.4816 N06600 NCF 600 МНЖМц 28-2,5-1,5 NiCr15Fe ЭИ868 CHEMICAL COMPOSITION OF Inconel N06600 Forgings: Grade C…

Grade:: 600
Standard:: ASTM B564
Surface:: Mill finish, pickled, polished, or as required
Diameter:: Not applicable

Send email to us

Product Detail

Product Tags

Specifications of Inconel 600 Forging:

Grade	600,601,625,690 etc.
Specifications	ASTM B564, AMS 5665
International Specifications	BS 3072-3076 (NA14) DIN 17742, DIN 17750, DIN 17754 WERKSTOFF Nr 2.4816 TÜV 305 AFNOR-NC 15 Fe

Other Type Of 600 Forged:

Inconel 600 Equivalent For Forgings:

STANDARD	WERKSTOFF NR.	UNS	JIS	GOST	EN	OR
600	2.4816	N06600	NCF 600	МНЖМц 28-2,5-1,5	NiCr15Fe	ЭИ868

CHEMICAL COMPOSITION OF Inconel N06600 Forgings:

Grade	C	Mn	Si	S	Fe	Ni	Cu	Cr
600	0.15	1.0	0.50	0.015	6.0-10.0	72.0	0.50	14.0-17.0

Inconel 600 Forged Mechanical Properties:

Density	Melting Point	Tensile Strength	Yield Strength	Elongation
8.47 g/cm3	1413 °C (2580 °F)	Psi – 95000 , MPa – 655	Psi – 45,000 , MPa – 310	45%

Physical Constants and Thermal Properies:

Property	Imperial Units	Metric Units
Density	0.306 lb/in³	8.47 g/cm³
Melting Range	2470 – 2575 °F	1354 – 1413 °C
Specific Heat	0.106 Btu/lb·°F	444 J/kg·°C
Curie Temperature	-192 °F	-124 °C
Permeability at 200 Oersted (15.9 kA/m)	1.010	–
Coefficient of Expansion (70–200°F / 21–93°C)	7.4 × 10⁻⁶ in/in·°F	13.3 µm/m·°C
Thermal Conductivity	103 Btu·in/ft²·h·°F	14.9 W/m·°C
Electrical Resistivity	620 ohm·circ mil/ft	1.03 µΩ·m

Typicat Mechanical Properties:

Property	Imperial Units	Metric Units
Tensile Strength	95 ksi	655 MPa
Yield Strength (0.2% Cƒ set)	45 ksi	310 MPa
Elongation	40%	—

SASA ALLOY'S Manufacturing Process for Forged Bars and rings:

The square/flat bars are made from ingots and are processed after giving required reduction ratio and discarding hot top and bottom for homogeneity. They are either processed by hot rolling or hot forging. These bars are further heat treated as per customer requirements by any one of the following processes

1.Annealing
2.Normalizing
3.Stress Relieving
4.Quenching and Tempering
5.Spheroidizing Annealing

Quality Check of Forged:

Following checks are conducted in bars/rings/step shafts and reported in the TEST CERTIFICATE as per customer requirement.
1.Surface inspection is carried out of each bar end to end
2.Positive Material Identification using XRF to certify in process chemistry of each bar
3.100% dimensional verification using calibrated verniers and Go No-4.Go gauges
5.Step down testing
6.Upset forging test
7.NMIR (Non metallic inclusion rating)
8.Macrostructure testing
9.Microstructure phase analysis
10.Grain Size
11.Ultrasonic Testing for internal defects
12.Radioactivity test
13.Gas analysis (O, N, H)

Why Choose Us:

Packing:

1. Packing is quite important especially in a case of international shipments in which consignment pass through various channels to reach the ultimate destination, so we put special concern regarding packaging.

2. Sasa alloy’s pack our goods in numerous ways based on the products. We pack our products in multiple ways, such as,