Monel K500 Wire

Short Description:

Monel K500 is a nickel-copper alloy known for its exceptional corrosion resistance, high strength, and durability. It contains roughly 63% nickel, 29% copper, 2.3% aluminum, and traces of iron and other elements. This alloy is often used in applications requiring resistance to seawater, chemicals, and high temperatures. Specifications of Monnel K500 Wire: Grade 400，K500 Standard ASTM B865 Length 100 mm TO 6000 mm, customizable Diameter 10…

Grade:: Monel K500
Standard:: ASTM B865 ASME SB865
Surface:: Bright, pickled, oxidized, or as required
Diameter:: 10 mm To 100 mm

Send email to us

Product Detail

Product Tags

Specifications of Monnel K500 Wire:

Grade	400，K500
Standard	ASTM B865
Length	100 mm TO 6000 mm, customizable
Diameter	10 mm To 100 mm or as per client requirement
Types	Filler Wire, Coil Wire, Electrode Wire, Welding Wire, Wire mesh, Knitted wire mesh, filter mesh, mig wire, tig wire, spring wire
Surface	Polished bright, Smooth
Technology	Cold Rolled, hot rolled

Type Of Monel K500 Wire:


Monel K500 Wire	Monel K500 Wire Mesh	Monel K500 Welding Wire

Monel K500 10 gauge welded Wire Mesh	Monel K500 Knitted Wire Mesh	Monel K500 Filler Wire

Monel K500 Coil Wire	Monel K500 Electrode Wire	Monel K500 Spool Wire

Equivalent Grades Of Monel K500 Wires:

STANDARD	WERKSTOFF NR.	UNS
Monel K500	2.4375	N05500

CHEMICAL COMPOSITION OF Monel K500 Wire:

Grade	C	Mn	Si	S	Fe	Ni	Cu
Monel K500	0.25	1.5	0.50	0.010	0.5-2.0	63.0	27.0-33.0

Monel K500 Wires Mechanical Properties:

Density	Melting Point	Tensile Strength	Yield Strength 0.2% Proof	Elongation (% in 50mm) (thick.>0.76mm)
8.44 g/cm3	1350 °C (2460 °F)	Psi – 160,000 , MPa – 1100	Psi – 115,000 , MPa – 790	20%

Physical Constants and Thermal Properties

Property	Imperial Units	Metric Units
Density	0.305 lb/in³	8.44 g/cm³
Melting Range	2400 – 2460 °F	1315 – 1350 °C
Specific Heat	0.100 Btu/lb·°F	419 J/kg·°C
Curie Temperature	-150 °F	-100 °C
Permeability at 200 Oersted (15.9 kA/m)	1.002	–
Coefficient of Expansion (70–200°F / 21–93°C)	7.6 × 10⁻⁶ in/in·°F	13.7 µm/m·°C
Thermal Conductivity	121 Btu·in/ft²·h·°F	17.5 W/m·°C
Electrical Resistivity	370 ohm·circ mil/ft	0.615 µΩ·m
Young’s Modulus at RT	26 × 10³ ksi	—

Typical Mechanical Properties (Precipitation Hardened)

Property	Imperial Units	Metric Units
Tensile Strength	160 ksi	1100 MPa
Yield Strength (0.2% Offset)	115 ksi	790 MPa
Elongation	20%	–

SASA ALLOY'S Quality Assurance:

1. Visual Dimension Test
2. Mechanical examining like tensile, Elongation and reduction of area.
3. Impact analysis
4. Chemical examination analysis
5. Hardness test
6. Pitting protection test
7. Penetrant Test
8. Intergranular Corrosion Testing
9. Roughness Testing
10. Metallography Experimental Test

Why Choose Us:

Packing:

1. Packing is quite important especially in a case of international shipments in which consignment pass through various channels to reach the ultimate destination, so we put special concern regarding packaging.
2. Sasa alloy’s pack our goods in numerous ways based on the products. We pack our products in multiple ways, such as,