Incoloy 800H
Alloy 800H has excellent corrosion resistance in the water media at extremely high temperature of 500℃. Its higher nickel content made it have good stress corrosion resistance cracking properties in the water corrosion condition. High chromium content made it better resistance to pitting and crevice corrosion cracking. This alloy can resist nitric acid and organic acid, but it is not so fine in the sulfuric acid and hydrochloric acid.
Specification
| UNS | W.Nr |
| N08810 | 1.4958 |
Chemical composition
| Grade | % | Ni | Cr | Fe | C | Mn | Si | Cu | S | Al | Ti | P |
| 800H | Min | 30 | 19 | Bal, | 0.05 | 0.15 | 0.15 | |||||
| Max | 35 | 23 | 0.10 | 1.5 | 1 | 0.75 | 0.015 | 0.60 | 0.60 | 0.03 |
Mechanical properties(Minimum value at 20℃)
| Tensile Strengthσb/MPa | Yield Strengthσp0.2/MPa | Elongationσ5 /% |
| 450 | 180 | 35 |
Standard
| Bar | Forging | Sheet/Strip | Wire | Pipe |
| ASTM B408 | ASTM B564 | ASTM B409 | ASTM B408 | ASTM B407ASTM B514 |