2014 T6 Aluminium Plate
2014 T6 Aluminium Plate have strong corrosion resistance characteristics and high electrical conductivity. The strength of Aluminium 2014 Plate increase at subzero temperatures and strength is lost when these alloys are exposed to high temperatures. Aluminium Plate 2014 T6 other name are Aluminium 2014-T651; UNS A92014; ISO AlCu4SiMg; BS H15 (UK); CSA CS41N (Canada); AA2014-T651, DIN AlCuSiMn; NF A-U4SG (France).
2014 T6 Aluminium Plate ASTM B209, ASTM-B-209, EN573, and EN485 international standards.
AMS 4029 Plate
Sasa alloy is the leading manufacturer and exporter of 2014 T6 Aluminium Plate. Supplier of ASTM B209 2014 T6 Aluminium Plate from 0.5mm to 5mm Thick 1000mm x 1000mm to 2500mm x 1250mm Tempers manufactured in accordance with international standards ASTM B209, ASTM-B-209, EN573, and EN485, check 2014 T6 Aluminium Plate price. The general widths of 2014 T6 H16 Aluminum Plates are 1000mm, 1250mm and 1500mm, while common lengths are 2000mm, 2500 mm and 3000mm respectively. Wholesale Trader of 2014 T6 Commercial Aluminium Plate offered by Sasa alloy , China. Stockist of 2014 T6 Aluminium Plate, H32 2014 T6 Aluminium Stucco Plate, H38 Commercial 2014 T6 Aluminium Plate, ASME SB209 2014 T6 Aluminium Patterned Plate, 2014 T6 Mill Finish, 2014 T6 Aluminium Extruded Plate, 2014 T6 Aluminium Plate and 2014 T6 Aluminium Plate in China.
2014 T6 Aluminium Plate Suppliers in UNS A92014 T6 Aluminium Plate stockist in China, 2014 T6 Aluminium Corrugated Plate Suppliers in Best Price of EN AW 2014 T6 H14 Aluminium Plate
You may intrested in:
- 2014 T6 Aluminium Chequered Plate
- 2014 T6 Aluminium Checker Plate
- 2014 T6 Aluminium Diamond Plate
- 2014 T6 Aluminium Tread Plate
Standard Dimensions of 2014 T6 Aluminium Plate
Standard dimensions (a x b) of Aluminium 2014 T6 Plate
Aluminium 2014 T6 Plate up to 9.9 mm
2.000 x 1.000 mm
2.500 x 1.250 mm
3.000 x 1.500 mm
Oversize Aluminium 2014 T6 Plate
4.000 x 2.000 mm
6.000 x 2.500 mm
8.000 x 2.500 mm
Other dimensions on request
2014 T6 Aluminium Plate Suppliers in China, 2014 T6 Aluminium Plate Supplier Singapore, Dealer & Distributor of All 2014 T6 Aluminium Alloy Plate Grades, Stockholder of 2014 T6 Aluminium Plate 1mm
| Aluminium Alloy | ASTM B209 2014 T6 |
| Aluminium 2014 T6 Plate Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium 2014 T6 Plate Thickness | 0.5mm-150mm |
| Aluminium 2014 T6 Plate Width | 500-2000mm |
| Aluminium 2014 T6 Plate Length | to clients’ requirement |
| Aluminium 2014 T6 Plate Coating | Polyester, Fluorocarbon, polyurethane and epoxy coating |
| 2014 T6 Aluminium Plate Coating finish | PVDF, POLYESTER(PE) |
| Aluminium 2014 T6 Plate Surface | Polished, hair line, brush, sand blast, checkered, embossed, etching, etc. Mill finish, Bright finish, paper interleaved, one side film, both sides film. |
| Aluminium 2014 T6 Plate Gloss | Meet the customer requirement |
| Total coating thickness of Aluminium 2014 T6 Plate | PVDF coating: More than 25 micron; Polyester coating: More than 18 micron |
| Aluminium 2014 T6 Plate Coating hardness | (pencil hardness) more than 2H |
| Aluminium 2014 T6 Plate Coating adhesive | No lower than1st grade |
| Aluminium 2014 T6 Plate Impact resistance | No cracking or peeling (50kg/cm, ASTMD-2794: 1993) |
| Aluminium 2014 T6 Plate Flexibility (T-bend) | 2T |
| Aluminium 2014 T6 Plate MEK resistance | More than 10 |
| Available Aluminium 2014 T6 Plate Stock Sizes | 1ft x 1ft, 1ft x 2ft, 1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size or Custom Shape. |
| Aluminium 2014 T6 Plate Delivery Time | 30-60 days after receiving the prepayment |
| Aluminium 2014 T6 Plate Packaging Details | Standard export package. One pallet is about 2-3 ton.Two steel belts in width and three in width. One 20GP container can load about 18-20 tons Aluminium 2014 T6 Plate. One 40GP container can load about 24 tons Aluminium 2014 T6 Plate |
| ASTM B209 Alloy 2014 T6 Plate Outer packing | Export standard, wooden pallet |
| Bottom side Aluminium 2014 T6 Plate is coated with protective polyester material, thickness more than 6 micron | |
| We Export Aluminium 2014 T6 Plate to | Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc. |
Types of 2014 T6 Aluminium Plate Manufacturer in China
| 2014 T6 Aluminium Plates Product Range | ||||
|---|---|---|---|---|
| Alloy No. | Thickness (mm) |
Width (mm) |
Length (mm) |
Temper |
| 2014 T6 Aluminium Plate | 0.2-5.0 | 20-2200 | 20-8000 | O, H12, H22, H14, H16, H18, H24, H26 |
Standard Specification of 2014 T6 Aluminium Plate
Standards and specifications by country
| Specification | Alloy | Temper | Company |
|---|---|---|---|
| Europe | |||
| EN 2089/2395 | 2014A | T6(T62)/T4(T42) | |
| EN 2087/2088 | 2014A clad | T6(T62)/T4(T42) | |
| France | |||
| AIR 9048.010/.030/ | 2014 | F(T42)/F(T62)/T4/ | |
| .020/.040/.050 | 2014 | T6/T451 | |
| AIR 9048.060/.080/.070/.090 | 2014 clad | F(T42)/F(T62)/T4/T6 | |
| Germany | |||
| W.-Nr. 3.1254 | 2014A | T4, T6 | |
| W.-Nr. 3.1354 | 2024 | O(T42), T3 | |
| UK | |||
| BS L156/157/158*/159* | 2014A | ||
| 158*/159* | 2014A clad | (T42)(T62) | BAE Systems |
| BS L163/164/165 | 2014A clad | T3/F(T42), T4/T6 | |
| BS L166*/167* | 2014A clad | F(T42), T4/T6 | |
| USA | |||
| AMS QQ-A-250/3 | 2014 clad | O, T4, T6 | |
| European Standard | BS (OLD) | USA (AA) | GERMANY (DIN) | ISO | IS | Canadian |
|---|---|---|---|---|---|---|
| EN AW-2014 | HE15 | 2014 | AlCuSiMn | AlCu4SiMg | 24345 | B26S |
2014 T6 Aluminium Plate Equivalent Grades
| China |
U.S.A. |
BRITAIN |
CANADA | GERMANY |
RUSSIA |
I.S.O. |
FRENCH | |
|---|---|---|---|---|---|---|---|---|
| New IS | Old IS | (A.A.) |
(B.S.) |
(DIN) | – | – | – | |
| 24345 | H15 | 2014 | H15 | B26S | Al-Cu-Si | AK | Al-Cu-4Mg Si | – |
2014 T6 Aluminium Plate Sizes
| Sizes (mm) | Theoretical Mass KG/Plate |
|---|---|
| 2000 X 1000 X 0.5 | 2500 X 1250 X 0.5 |
| 2000 X 1000 X 0.7 | 2500 X 1250 X 0.7 |
| 2000 X 1000 X 0.9 | 2500 X 1250 X 0.9 |
| 2000 X 1000 X 1.2 | 2500 X 1250 X 1.2 |
| 3000 X 1500 X 1.2 | 2000 X 1000 X 1.6 |
| 2500 X 1250 X 1.6 | 3000 X 1500 X 1.6 |
| 2000 X 1000 X 2.0 | 2500 X 1250 X 2.0 |
| 3000 X 1500 X 2.0 | 2500 X 1250 X 2.5 |
| 2.79 | 4.36 |
| 3.91 | 6.10 |
| 5.02 | 7.85 |
| 6.74 | 10.46 |
| 15.01 | 8.93 |
| 13.95 | 20.09 |
| 11.16 | 17.44 |
| 25.11 | 21.80 |
2014 T6 Aluminium Plate Weight Chart
Width: 1.000 mm | Length: 2.000 mm
| Product | Thickness | Weight |
|---|---|---|
| 2014 T6 Aluminium Plate | 0,30 mm | 0,810 Kg/m2 |
| 2014 T6 Aluminium Plate | 0,40 mm | 1,080 Kg/m2 |
| 2014 T6 Aluminium Plate | 0,50 mm | 1,350 Kg/m2 |
| 2014 T6 Aluminium Plate | 0,60 mm | 1,620 Kg/m2 |
| 2014 T6 Aluminium Plate | 0,70 mm | 1,890 Kg/m2 |
| 2014 T6 Aluminium Plate | 0,80 mm | 2,160 Kg/m2 |
| 2014 T6 Aluminium Plate | 0,90 mm | 2,430 Kg/m2 |
| 2014 T6 Aluminium Plate | 1,00 mm | 2,700 Kg/m2 |
| 2014 T6 Aluminium Plate | 1,20 mm | 3,240 Kg/m2 |
| 2014 T6 Aluminium Plate | 1,40 mm | 3,780 Kg/m2 |
| 2014 T6 Aluminium Plate | 1,50 mm | 4,050 Kg/m2 |
| 2014 T6 Aluminium Plate | 1,60 mm | 4,320 Kg/m2 |
| 2014 T6 Aluminium Plate | 1,80 mm | 4,860 Kg/m2 |
| 2014 T6 Aluminium Plate | 2,00 mm | 5,400 Kg/m2 |
| 2014 T6 Aluminium Plate | 2,20 mm | 5,940 Kg/m2 |
| 2014 T6 Aluminium Plate | 2,50 mm | 6,750 Kg/m2 |
| 2014 T6 Aluminium Plate | 3,00 mm | 8,100 Kg/m2 |
| 2014 T6 Aluminium Plate | 4,00 mm | 10,800 Kg/m2 |
| 2014 T6 Aluminium Plate | 5,00 mm | 13,500 Kg/m2 |
| 2014 T6 Aluminium Plate | 6,00 mm | 16,200 Kg/m2 |
| 2014 T6 Aluminium Plate | 10,00 mm | 27,000 Kg/m2 |
| 2014 T6 Aluminium Plate | 12,00 mm | 32,400 Kg/m2 |
| 2014 T6 Aluminium Plate | 15,00 mm | 40,500 Kg/m2 |
| 2014 T6 Aluminium Plate | 20,00 mm | 54,000 Kg/m2 |
2014 T6 Aluminium Plate Chemical Composition
| Alloy (ISS) | Equivalent alloy (A.A) | Copper | Magnesium | Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Old | New | U.S.A | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
| H 15 | 24345 | 2014 | 3.8 | 5.0 | 0.2 | 0.8 | 0.5 | 1.2 | 0.7 | 0.3 | 1.2 | 0.5 | — | ||
Aluminium 2014 T6 Plate Mechanical Properties
| Alloy | Temper | UTS (Mpa) | Yield Strength (Mpa) | Elongation (%) | ||
|---|---|---|---|---|---|---|
| Minimum | Maximum | Minimum | Maximum | A 50mm (Minimum) | ||
| EN AW-2014 | O | – | 250 | – | 135 | 10 |
| T4 | 370 | – | 230 | – | 11 | |
Equivalent materials to Aluminium / Aluminum 24345 alloy are given in the table below.
| ASTM B210 | ASTM B211 | ASTM B221 | ASTM B241 | ASTM B247 |
| ASTM BB241 | DIN 3.1255 | MIL T-15089 | QQ A-200/2 | QQ A-225/4 |
| QQ A-250/4 | QQ A-367 | SAE J454 |
Aluminum Alloy Heat Treatment Temper Designations
Basic Aluminum Heat Treatment Designations
- F As Fabricated
- O Annealed
- H Strain Hardened
- W Solution Heat Treated
- T Solution Heat Treated
Heat Treating T Temper Codes for Aluminium 2014 T6 Plates
- T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
- T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
- T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
- T4 – Solution heat treated, and naturally aged to a substantially stable condition.
- T5 – Cooled from an elevated temperature shaping process then artificially aged.
- T6 – Solution heat treated then artificially aged.
- T7 – Solution heat treated then overaged/stabilized.
- T8 – Solution heat treated, cold worked, then artificially aged.
- T9 – Solution heat treated, artificially aged, then cold worked.
- T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.
Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.
H Temper Strain Hardening Codes for Aluminium 2014 T6 Plates
- H1 – Strain hardened only
- H2 – Strain hardened and partially annealed
- H3 – Strain hardened and stabilized
- H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.
2014 T6 Plate Packing Information of Aluminum plate :
Application of 2014 T6 Aluminium Plate
2014 T6 Aluminium Plate is the most widely used form of Industrial Aluminium. 2014 T6 Aluminium Plates find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.